Base composition:
 Good things up BingJie board is 100% free of asbestos fibers.
1. The substrate important ingredient: the Portland cement, quartz sand, imported wood pulp as raw material by mixing, made embryo plate 14,000 tons high pressure, high temperature steam curing made by enclosed.
2. The base level of fire: A1 (the highest level)
3. Good things up BingJie fancy plate, model, price
A, there are all kinds of wood, Shiwen, bamboo pattern, sticks, parquet, qualities, etc. more than 6000 kinds, any customer choice; and to meet the individual needs of designers, pattern or design can offer customers tailor build.
B, BingJie board fancy currently temporarily introduced some classic fancy, there are high-gloss, matt, embossed surface, while supporting the production and finishes the same color, the same pattern of various income side lines.
C, type of establishment, size selected, the price development is still in progress, is expected to introduce in mid-July. Currently provisional specification: 1220 × 2440 × 4.5.6
The company has introduced advanced cutting, milling, side with color shading equipment, and supporting the lines and the like.
4. Applications :( mainly indoor finishes)
A, Decoration: wall replace marble, granite, ceramic tile, wood finishes; TV backdrop
B, tooling: offices, clubs, hotels, restaurants, entertainment, etc.
C, urban underground tunnels, subway stations, air defense projects and other municipal facilities.
5. Product installation and support lines:
A, tightly sewn assembly
B, aluminum installation (included profiles)
C, the left seam sealing practices
D, matching the same color line installation method, construction node graph and physical samples show presentation
 
The substrate of the technical parameters:
1. density substrate in 1.4-1.7g / cm3, the density of the base plate at present I am using are ≥1.5 g / cm3
2. Water absorption ≤25% (good things up BingJie board after the double-treated substrate does not exist water absorption, which can say no absorption)
Material moisture content ≤12% 3. The company uses both ≤10%
The swelling rate ≤0.23% (wool board wet base inflation rate is generally about 0.15%, is negligible, meaning that small changes after the experiment)
5. The flexural strength (dry state) average flexural strength 6mm thick sheet of 34.38MPa (MPa), 9mm thick sheet the average flexural strength of 31.19MPa, good things up BingJie finished by the base plate than the original factory test substrate flexural strength increased by 2.05 times, while the other general direct printing, stamping, painting board, UV board decorative plates and flexural strength of small changes.
Impact strength: 6mm plate: horizontal impact strength 8.0707kJ / m2 on average 6.77 kJ / m2 (kJ / per square)
                            Longitudinal impact strength 5.4723kJ / m2 average 6.77k J / m2
2.71 times the impact strength
               9mm plate: horizontal impact strength 9.0477kJ / m2 average 7.38kJ / m2
                            Longitudinal impact strength 5.7047kJ / m2 average 7.38k J / m2
2.95 times the impact strength
6. Weight: The weight calculation formula:
Plate thickness (mm) × 1.55 (density) × 1.1 (10% moisture content) = kg / m2
Plate thickness (cm) × 1.55 (density) × 1.1 (10% moisture content) × 2.98 (1 张 board squared) = kg / Zhang
Example: take 5 planks:. 5 × 1 55 × 1.1 × 2.98 = 25.4kg / Zhang
            9 planks:. 9 × 1 55 × 1.1 = 45.728 kg / Zhang
          12 planks:. 12 × 1 55 × 1.1 = 60.9 kg / Zhang
7. surface wear resistance: 700 rpm
8. High temperature: 120 ° C test results after two childhood best BingJie board did not change things up, not from the shell off phenomenon, and other similar products are from the shell off phenomenon.
9. resistance to discoloration: the weathering test chambers after two hours of good things BingJie plate change, and other similar products have obvious discoloration